FastFire 15
Universal phosphate investment for all
crown and bridge alloys
|
| |
FastFire 15 is a fine-grain phosphate
investment which requires only a
15-minute benchset before placing
molds into a hot oven for rapid
burnout. It produces accurate,
smooth castings using either the
ringless or metal ring technique.
Optimum fit is achieved for all crown
and bridge alloys through dilution of
the freeze stable FastFire Liquid. |
|
|
|
| |
| Features: |
- Produces castings in less than one
hour.
- FastFire Liquid allows year
round, problem-free shipping and
controlled expansion.
- Reliable performance using many
casting techniques and alloys.
- Exceptionally smooth, accurate
castings. |
| |
Physical Properties |
| Liquid/Powder Ratio |
27 ml/100 g |
| Working Time |
7-9 minutes |
| Setting Expansion |
1.0% |
| Thermal Expansion |
1.0% |
| Compressive Strength, Wet |
500 psi (3.4 MPa) |
|
| |
|
|
| |
------------------------------------------------------------------------------------------------------------------------------------------------------------------------ |
| |
AccuVest
Investment for non-precious alloys
|
| |
AccuVest is an economical fine-grain phosphate investment which requires only a 30-minute
benchset before placing molds into a hot oven for rapid burnout. It produces accurate, smooth
castings using either the ringless or metal ring technique. Optimum fit is achieved for all crown
and bridge alloys through dilution of the Special Liquid Concentrate MAX. |
|
|
|
| |
| Features: |
- Produces castings in less than one hour.
- Extremely consistent results.
- Robust formula, gives increased strength during burnout.
- Reliable performance using many casting techniques and alloys.
- Exceptionally smooth, accurate castings. |
| |
Physical Properties |
| Liquid/Powder Ratio |
20 ml/100 g |
| Working Time |
7-9 minutes |
| Setting Expansion |
2.50% |
| Thermal Expansion |
1.20% |
| Compressive Strength, Wet |
600 psi (4 MPa) |
|
| |
|
------------------------------------------------------------------------------------------------------------------------------------------------------------------------
|
| |
X-20 Speed
A Phosphate investment for casting
partials with chromium dental alloys |
| |
Improved casting investment for
making Chrome partial denture
frameworks in half the time.
- Outer mold ready for burnout after
20 minutes
- Recommended liquid:
Special Liquid Concentrate,
Sold separately |
|
|
|
| |
Physical Properties |
| Liquid/Powder Ratio |
12 ml/100 g |
| Working Time |
5-6 minutes |
| Ready for Separating |
N/A |
| Ready for Burnout |
20 minutes |
| Setting Expansion |
0.10% |
Thermal Expansion
700°–1,000° C (1,300°–1,800° F) |
1.00% |
| Compressive Strength, wet |
1,850 psi (13 MPa) |
|
| |
------------------------------------------------------------------------------------------------------------------------------------------------------------------------ |
Investments
Accurate in precision and handling
Dentaurum covers a whole spectrum of techniques with its large range of investment material. Whether for metal dentures or crown and bridge techniques, whether for the conventional method or for speed heating, whether for precious metal alloys, non-precious metal alloys or titanium, the world's largest manufacturer of investment materials can offer the correct investment for each individual technique. |
| |
Castorit® all speed
C+B speed investment for all precious and non-precious alloys |
| |
- |
Mould can be placed into the furnace at final temperature (950°C) for speed preheating or preheated in stages overnight. |
- |
For the entire range of applications and all types of alloy from precious metals to high expansion non-precious alloys. |
- |
The high overall expansion provides precision of fit, even for telescopic restorations. |
- |
Handles very easily - Long working times and very creamy consistency after mixing. |
- |
Castings with extremely smooth surfaces ensure uniform quality and exact reproduction of the pattern |
|
| |
|
| |
Investments
fast, flexible and perfect fit
Dentaurum investment materials cover the whole spectrum of cast partial denture technique. They can be used for the conventional preheating overnight, however the ring can be placed into the furnace at final temperature. |
| |
Rema® Exakt F
Fine and exact model casting investment material |
| |
- |
Improved development of the classic rema® Exakt: The well proven recipe was optimized with a finer grain size. |
- |
very easy, pleasant working:
+ amenable consistency
+ adequate working time
+ reduced dust |
- |
Very high accuracy: perfectly fitting castings in all areas. |
- |
Especially light divestment: very soft divestment and light sandblasting. |
|
| |
|
| |
|